Fused quartz is manufactured from deliberated silica sand,through high termperature fusion,cooling,smash and selecting. Fused Quartz LumpFused quartz is manufactured from deliberated silica sand,through high termperature fusion,cooling,smash and selecting,the appearance is...

Fused Silica is manufactured from deliberated silica sand,through high termperature fusion,cooling,smash and selecting. Fused SilicaFused Silica is manufactured from deliberated silica sand,through high termperature fusion,cooling,smash and selecting,the appearance is colorless...

Silex; Silica SiO2: 99.13% Alumina Al2O3: 0.36% grain size: 0-5mm use: clean the melting iron Silex;Chemical analysisSilica SiO2: 99.13%Alumina Al2O3: 0.36%Iron Oxyde Fe2O3: 0.18%Magnesia MgO: 0.04%Lime CaO: 0.09%grain size: 0-5mmuse: clean the melting iron  ...

Corundum based high strength refractory castables refractory castables castables refractory Corundum based high strength refractory castablesBrandCorundum based high strength refractory castablesservice temperature °C1800°CChemical composition(%)Al2O394% MinCaO2.0%...

Alkali resistant Fire clay bricks for cement kiln and fireclay bricks for Hot-blas furnaces Fire Clay Alkali Resistant BricksAL2O338-40%Fe2O32.0% maxBulk density2.15Refractoriness1750°C0.2Mpa refractoriness under load1407°CLinear change after...

Magnesia Spinel Bricks MLJ85A shape B220 MLJ85A shape B420 Magnesia Spinel BricksMLJ85A shape B220MLJ85A shape B420MgO%86.30AL2O3%9.80Fe2O3%0.62SiO2%0.57Apparent Porosity%16Bulk Densityg/cm³3.0Cold Crushing StrengthMpa550.2Mpa Refractoriess under load°C1700Thermal shock...

Calcium Aluminate CaO 49-54% Al2O3:40-45% Sio2:2.8% max Size:5-25mm 90% m Calcium AluminateCaO49-54%Al2O340-45%Sio22.8% maxTio22.7% maxMgO2.0% maxFe2O31.5% maxMelting Point1380 deg CParticle size5-25 mm   90% minPre-fused clinker for refined steel-making is newly...

Dense Refractory Castable for circulation fluidized bed boiler(CFBC castable) Refractory low cement castable for boiler Dense Refractory Castable for circulation fluidized bed boiler(CFBC castable)BrandGT-30service temperature °C1800°CChemical composition(%)Al2O394%...

Castable Dense Cast Low Cement Base on Tublaralum Sinter GT-90 Castable Dense Cast Low Cement Base on Tublaralum Sinter GT-90Technical data sheetBrandGT-90Max service temp.(°C)1800Bulk density(g/cm3)3.00Chemical composition(%)Al2O393.0 MinSiO25.0 MaxCaO1.5 MaxFe2O30.1MaxCold...

Pure Corundum based high strength refractory castables Corundum based high strength refractory castablesBrandCorundum based high strength refractory castablesservice temperature °C1800°CChemical composition(%)Al2O394% MinCaO2.0% MaxFe2O30.2% MaxBulk density(g/cm3)3.00Cold...